S-Plastics Ultem 9085 resin is High flow Polyimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 84 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 74 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 72 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3440 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 138 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2920 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 88 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 71 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 6.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3050 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2750 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 115 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 0 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 0 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 0 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 0 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 153 | °C | ASTM D 648 |
| CTE, -20°C to 150°C, flow | 0.E+00 | 1/°C | ASTM E 831 |
| CTE, -20°C to 150°C, xflow | 0.E+00 | 1/°C | ASTM E 831 |
| CTE, 23°C to 150°C, flow | 0.E+00 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 0.E+00 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 0 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 173 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.34 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 295°C/6.6 kgf | 8.9 | g/10 min | ASTM D 1238 |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.39 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.17 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 65 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| FAA Flammability, FAR 25.853 A/B | <5 | - | FAR 25.853 |
| OSU total heat release (2 minute test) | 16 | kW-min/m² | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 36 | kW/m² | FAR 25.853 |
| Vertical Burn a (60s) passes at | 2 | sec | FAR 25.853 |
| Oxygen Index (LOI) | 49 | % | ASTM D 2863 |
| Source GMD, last updated:01/19/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 135 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 330 - 350 | °C |
| Nozzle Temperature | 330 - 350 | °C |
| Front - Zone 3 Temperature | 330 - 350 | °C |
| Middle - Zone 2 Temperature | 325 - 345 | °C |
| Rear - Zone 1 Temperature | 315 - 340 | °C |
| Mold Temperature | 120 - 150 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:01/19/2007 | ||
|
For more information please download the datasheet |
|
 |