S-Plastics Xenoy 6380U resin is a 30% glass reinforced, UV stabilized grade, that combines high stiffness with improved ductility. The combination of mechanical properties at high and low temperatures and chemical resistance makes XENOY 6380U a suitable material for a wide range of demanding applications where safety is a primary consideration. The material´s gloss characteristics are an added advantage for appearance parts in the appliance industry.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 100 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 100 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 8200 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 140 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7000 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8400 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7200 | MPa | ISO 178 |
| Hardness, H358/30 | 115 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 110 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D 4812 |
| Izod Impact, unnotched, -30°C | 600 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 60 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 7 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 180 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 165 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.3E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 180 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.51 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.3 - 0.7 | % | S-Plastics Method |
| Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/1.2 kgf | 13 | g/10 min | ASTM D 1238 |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.5 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+14 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 1.6 mm | 20 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 4.2 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 4 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 750°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Source GMD, last updated:05/04/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 265 - 285 | °C |
| Nozzle Temperature | 260 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 250 - 275 | °C |
| Rear - Zone 1 Temperature | 240 - 270 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 110 | °C |
| Source GMD, last updated:05/04/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy 6380U.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|