S-Plastics Stat-kon ZX08301 resin is a high heat compounds with ESD safe and low warpage performance suitable for use in Semiconductor
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 120 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 11000 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 162 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9000 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 46 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 200 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 194 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 5.6E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.29 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.2 - 0.35 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.3 - 0.45 | % | ASTM D 955 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 5.5E+05 - 7.5E+05 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.1E+05 - 2.5E+05 | Ohm | ASTM D 257 |
| Static Decay, 5000V to <50V | 0.1 | < seconds | FTMS101B |
| Source GMD, last updated:2009/08/18 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 | °C |
| Drying Time | 3 - 5 | hrs |
| Melt Temperature | 295 - 305 | °C |
| Nozzle Temperature | 290 - 295 | °C |
| Front - Zone 3 Temperature | 300 - 305 | °C |
| Middle - Zone 2 Temperature | 290 - 295 | °C |
| Rear - Zone 1 Temperature | 280 - 285 | °C |
| Mold Temperature | 90 | °C |
| Back Pressure | 9 | MPa |
| Screw Speed | 100 | rpm |
| Source GMD, last updated:2009/08/18 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon ZX08301.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|