S-Plastics Stat-kon Cycoloy_EXCP0207 resin is SINGLE LOT DATA, 10% carbon fiber reinforced nonhalogenated FR PC+ABS for applications requiring ESD or low to moderate EMI-
shielding.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 74 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 74 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 8960 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 122 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7100 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 256 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 48 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 11 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 98 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 94 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.25 | - | ASTM D 792 |
| Source GMD, last updated:07/15/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 245 - 275 | °C |
| Nozzle Temperature | 245 - 275 | °C |
| Front - Zone 3 Temperature | 245 - 275 | °C |
| Middle - Zone 2 Temperature | 220 - 265 | °C |
| Rear - Zone 1 Temperature | 220 - 255 | °C |
| Mold Temperature | 60 - 80 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 30 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:07/15/2002 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |