S-Plastics Stat-kon LC-1003 EM resin is a compound based on Polyketone resin containing Carbon Fiber. Added features of this
material include: Easy Molding.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 160 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11510 | MPa | ASTM D 638 |
| Flexural Stress | 259 | MPa | ASTM D 790 |
| Flexural Modulus | 9510 | MPa | ASTM D 790 |
| Tensile Stress, break | 163 | MPa | ISO 527 |
| Tensile Strain, break | 1.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10520 | MPa | ISO 527 |
| Flexural Stress | 263 | MPa | ISO 178 |
| Flexural Modulus | 9850 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 400 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 4 | J | ASTM D 3763 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 270 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 5.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 5.36E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 5.19E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.36E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 298 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.33 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.07 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.6 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.28 - 0.31 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.51 - 0.58 | % | ISO 294 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+03 - 1.E+07 | Ohm | ASTM D 257 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.1 | % |
| Melt Temperature | 380 - 390 | °C |
| Front - Zone 3 Temperature | 380 - 395 | °C |
| Middle - Zone 2 Temperature | 365 - 375 | °C |
| Rear - Zone 1 Temperature | 350 - 360 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon LC-1003 EM.pdf |
|