S-Plastics Stat-kon Noryl_FMC3008A resin is a 30% carbon fiber/glass/mineral filled, static dissipative, foamable resin. UL94 V1 rated.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 20 | % | - |
| Tensile Stress, yield, 6.35 mm | 48 | MPa | ASTM D 638 |
| Tensile Strain, break, 6.35 mm | 3.5 | % | ASTM D 638 |
| Flexural Stress, yield, 6.4 mm | 102 | MPa | ASTM D 790 |
| Flexural Modulus, 6.4 mm | 7790 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| FOAM - IMPACT 6.4 mm Wt Reduction | 20 | % | - |
| Izod Impact, unnotched, 23°C, 6.4mm | 101 | J/m | ASTM D 4812 |
| THERMAL | Value | Unit | Standard |
| FOAM - THERMAL 6.4mm Wt Reduction | 20 | % | - |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 116 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 108 | °C | ASTM D 648 |
| Relative Temp Index, Elec | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 20 | % | - |
| Specific Gravity | 1.28 | - | ASTM D 792 |
| Specific Gravity, foam molded | 1.02 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.15 - 0.25 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.15 - 0.35 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| FOAM - ELECTRICAL 6.4 mm Wt Reduction | 20 | % | - |
| Volume Resistivity | 1.E+04 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+05 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| FOAM - Flame Class Minimum Density | 1.15 | g/cm³ | - |
| UL Recognized, 94V-0 Flame Class Rating (3) | 3.98 | mm | UL 94 |
| Source GMD, last updated:02/08/1993 | |||
| Parameter | ||
| Structural Foam Molding | Value | Unit |
| Blowing Agent, Physical System | Nitrogen Gas | - |
| Blowing Agent, Chemical System | FNC30X | - |
| Concentration Range (Blowing Agent) | 1 - 3 | % |
| Recommended Concentration (Blowing Agent) | 2 | % |
| Drying Temperature (Resin) | 105 - 110 | °C |
| Drying Time (Resin) | 2 - 4 | hrs |
| Drying Time (Resin, Cumulative) | 8 | hrs |
| Melt Temperature | 270 - 300 | °C |
| Nozzle Temperature | 270 - 300 | °C |
| Front Temperature | 270 - 300 | °C |
| Middle Temperature | 270 - 290 | °C |
| Rear Temperature | 260 - 280 | °C |
| Mold Temperature | 70 - 95 | °C |
| Source GMD, last updated:02/08/1993 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon Noryl_FMC3008A.pdf |
|