S-Plastics Stat-kon Noryl_HMC3008A resin is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 99 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 104 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 127 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 9850 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 120 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 77 | mg/1000cy | ASTM D 1044 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 149 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 121 | °C | ASTM D 648 |
| Relative Temp Index, Elec | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.28 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.06 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.05 - 0.15 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.15 - 0.3 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+03 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+05 | Ohm | ASTM D 257 |
| Static Decay, 5000V to <50V | 0.01 | < seconds | FTMS101B |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-1 Flame Class Rating (3) | 2.48 | mm | UL 94 |
| Oxygen Index (LOI) | 39 | % | ASTM D 2863 |
| Source GMD, last updated:03/15/1999 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 100 - 105 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 300 | °C |
| Nozzle Temperature | 270 - 300 | °C |
| Front - Zone 3 Temperature | 260 - 300 | °C |
| Middle - Zone 2 Temperature | 250 - 295 | °C |
| Rear - Zone 1 Temperature | 240 - 290 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 30 - 70 | % |
| Vent Depth | 0.038 - 0.051 | mm |
| Source GMD, last updated:03/15/1999 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon Noryl_HMC3008A.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|