S-Plastics Stat-kon Noryl_MX5840 resin is PRELIMINARY DATA. 18% carbon filled PPE+PS. Conductive, high heat. Will be commercialized as NCP1818.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 67 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 61 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 11 | % | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 143 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3680 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 120 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1046 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 8 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 186 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 172 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.15 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.6 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.6 - 0.8 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/5.0 kgf | 4.8 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:02/12/2001 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300 - 325 | °C |
| Nozzle Temperature | 300 - 325 | °C |
| Front - Zone 3 Temperature | 290 - 325 | °C |
| Middle - Zone 2 Temperature | 275 - 320 | °C |
| Rear - Zone 1 Temperature | 265 - 315 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 30 - 70 | % |
| Source GMD, last updated:02/12/2001 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon Noryl_MX5840.pdf |
|