S-Plastics Stat-kon EE004 resin is a compound based on Polyimide resin containing Carbon Fiber. Added features of this material include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 170 | MPa | ASTM D 638 |
| Tensile Strain, break | 2 | % | ASTM D 638 |
| Flexural Stress | 259 | MPa | ASTM D 790 |
| Flexural Modulus | 12330 | MPa | ASTM D 790 |
| Tensile Stress, break | 175 | MPa | ISO 527 |
| Tensile Strain, yield | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14500 | MPa | ISO 527 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Flexural Modulus | 12000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 534 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 212 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.34 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.5 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.5 | % | ISO 294 |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02 - 1.E+06 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.5 | mm | UL 94 by GE |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 360 - 365 | °C |
| Front - Zone 3 Temperature | 365 - 375 | °C |
| Middle - Zone 2 Temperature | 355 - 365 | °C |
| Rear - Zone 1 Temperature | 345 - 355 | °C |
| Mold Temperature | 120 - 150 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon EE004.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|