S-Plastics Stat-kon FX98500 resin is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 23 | MPa | ASTM D 638 |
| Tensile Stress, break | 13 | MPa | ASTM D 638 |
| Tensile Strain, yield | 15.8 | % | ASTM D 638 |
| Tensile Strain, break | 43.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1070 | MPa | ASTM D 638 |
| Flexural Stress | 26 | MPa | ASTM D 790 |
| Flexural Modulus | 870 | MPa | ASTM D 790 |
| Tensile Stress, yield | 23 | MPa | ISO 527 |
| Tensile Stress, break | 14 | MPa | ISO 527 |
| Tensile Strain, yield | 14 | % | ISO 527 |
| Tensile Strain, break | 82.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 870 | MPa | ISO 527 |
| Flexural Stress | 27 | MPa | ISO 178 |
| Flexural Modulus | 930 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | No break | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 48 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 21 | J | ASTM D 3763 |
| Multiaxial Impact | 63 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 46 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 48 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 0.976 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.02 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 2.7 - 3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.9 - 2.2 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 2.7 - 3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.9 - 2.2 | % | ISO 294 |
| Density | 0.97 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.02 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02 - 1.E+05 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+02 - 1.E+05 | Ohm | ASTM D 257 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 230 | °C |
| Front - Zone 3 Temperature | 220 - 230 | °C |
| Middle - Zone 2 Temperature | 210 - 220 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 40 - 55 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon FX98500.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|