S-Plastics Xenoy EXXY0054 resin is Low temperature Impact, High Flow Xenoy for Automotive Energy Absorbers
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 44 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 39 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 137 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1880 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 67 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2060 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 635 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 555 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 146 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 74 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.86 - 0.88 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/5.0 kgf | 15.8 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:10/28/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 275 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 245 - 265 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Mold Temperature | 40 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 80 | rpm |
| Shot to Cylinder Size | 50 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:10/28/2004 | ||