S-Plastics Stat-kon OEL13I resin is a Linear-PPS base resin containing Carbon Fiber and PTFE Lubricant. Characteristics of this grade are High Impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 132 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13950 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 195 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 10510 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 130 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 16590 | MPa | ISO 527 |
| Flexural Stress | 218 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 11920 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 601 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 93 | J/m | ASTM D 256 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 16 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 273 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 213 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 1.4E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 6.E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 212 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.37 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D 955 |
| Density | 1.37 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+00 - 3.E+00 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 2.E+00 - 4.E+00 | Ohm | ASTM D 257 |
| Surface Resistivity, ROA | 1.E+00 - 3.E+00 | Ohm | IEC 60093 |
| Source GMD, last updated:11/25/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 315 - 320 | °C |
| Front - Zone 3 Temperature | 330 - 345 | °C |
| Middle - Zone 2 Temperature | 320 - 330 | °C |
| Rear - Zone 1 Temperature | 305 - 315 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:11/25/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon OEL13I.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|