S-Plastics Xenoy EXXY0088 resin is a semi crystalline, reinforced PC+PBT blend, with an very high stiffness - ductility balance combined with good chemical resistance.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 62 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 40 | MPa | ISO 527 |
| Tensile Stress, yield, 50 mm/min | 67 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 50 | % | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 98 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3450 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Multiaxial Impact | 110 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, -30°C to 80°C, flow | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 131 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 134 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 120 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 97 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.7 - 0.9 | % | S-Plastics Method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 6 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/04/2006 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 270 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 240 - 265 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 80 | °C |
| Source GMD, last updated:08/04/2006 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy EXXY0088.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|