S-Plastics Stat-kon RE004MPC resin is a compound based on Nylon 6/6 resin containing carbon fiber. Characteristics of this grade are:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 130 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 21810 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 168 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6660 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 127 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 5.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13860 | MPa | ISO 527 |
| Flexural Stress | 207 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9850 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 947 | J/m | ASTM D 4812 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 8 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 60 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 250 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 209 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 2.42E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 8.97E+01 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 243 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 209 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.25 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.84 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.3 - 0.5 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 1 - 3 | % | ASTM D 955 |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.84 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 3.E+00 - 5.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:2009/06/09 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/06/09 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |