S-Plastics Stat-kon REP349 resin is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 167 | MPa | ASTM D 638 |
| Tensile Stress, break | 167 | MPa | ASTM D 638 |
| Tensile Strain, yield | 1.8 | % | ASTM D 638 |
| Tensile Strain, break | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 19300 | MPa | ASTM D 638 |
| Flexural Stress | 255 | MPa | ASTM D 790 |
| Flexural Modulus | 15160 | MPa | ASTM D 790 |
| Tensile Stress, yield | 168 | MPa | ISO 527 |
| Tensile Stress, break | 168 | MPa | ISO 527 |
| Tensile Strain, yield | 1.7 | % | ISO 527 |
| Tensile Strain, break | 1.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 18170 | MPa | ISO 527 |
| Flexural Stress | 263 | MPa | ISO 178 |
| Flexural Modulus | 15300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 576 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 5 | J | ASTM D 3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 34 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 250 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 232 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.26E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 251 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 234 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.54 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.4 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.18 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.67 | % | ISO 294 |
| Density | 1.54 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+07 - 1.E+09 | Ohm | ASTM D 257 |
| Source GMD, last updated:09/24/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon REP349.pdf |
|