S-Plastics Xenoy HX6600HP resin is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 35 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1900 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 43 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1900 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 44 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 37 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1900 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 64 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 800 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 750 | J/m | ASTM D 256 |
| Multiaxial Impact | 100 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 100 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 -40°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 65 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 70 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 117 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 60 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, flow | 1.3E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 117 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 120 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 60 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.21 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 1.2 - 1.6 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/5.0 kgf | 11 | g/10 min | ASTM D 1238 |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.4 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 10 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 210 | Pa-s | ISO 11443 |
| Source GMD, last updated:03/14/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 270 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 240 - 265 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 80 | °C |
| Source GMD, last updated:03/14/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy HX6600HP.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|