S-Plastics Xenoy X6800BM resin is Blow moldable, impact modifed XENOY
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 35 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 11 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 238 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1690 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 51 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1650 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 31 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 38 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 14.4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 167 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1700 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 48 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1420 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 802 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 186 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 54 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 95 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 22 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 129 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 115 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 47 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.7E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 8.3E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.7E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 115 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 46 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.22 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 2.85 - 3.35 | % | S-Plastics Method |
| Melt Flow Rate, 265°C/2.16kg | 4 | g/10 min | ASTM D 1238 |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.01 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 9 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:04/27/2007 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 100 - 105 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.01 - 0.03 | % |
| Melt Temperature (Parison) | 255 - 265 | °C |
| Barrel - Zone 1 Temperature | 250 - 260 | °C |
| Barrel - Zone 2 Temperature | 250 - 260 | °C |
| Barrel - Zone 3 Temperature | 255 - 260 | °C |
| Barrel - Zone 4 Temperature | 255 - 265 | °C |
| Adapter - Zone 5 Temperature | 255 - 265 | °C |
| Head - Zone 6 - Top Temperature | 255 - 265 | °C |
| Head - Zone 7 - Middle Temperature | 255 - 265 | °C |
| Head - Zone 7 - Bottom Temperature | 255 - 265 | °C |
| Screw Speed | 15 - 50 | rpm |
| Extruder Feed Zone Temperature | 255 - 265 | °C |
| Accumulator Temperature | 255 - 265 | °C |
| Mold Temperature | 50 - 95 | °C |
| Die Temperature | 255 - 265 | °C |
| Source GMD, last updated:04/27/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy X6800BM.pdf |
|