S-Plastics Xenoy XD549S resin is is an automotive grade, designed for thin wall (2.5 mm.) direct gated exterior parts. The material has an excellent flow. Xenoy XD549S can be painted with primerless solvent or waterbased paint systems. This grade has similar performance as CL300.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| Hardness, H358/30 | 95 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 49 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 30 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 26 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.18 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 8.6E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 123 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 127 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 100 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 75 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.7 - 1.1 | % | S-Plastics Method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.5 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Flow Rate, 250°C/2.16 kg | 14 | g/10 min | ISO 1133 |
| Melt Flow Rate, 250°C/5.0 kg | 40 | g/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 13 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 37 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+14 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| FMVSS Burning Speed, thickness 1 mm | 50 | mm/min | FMVSS 302 |
| Source GMD, last updated:12/14/1999 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 270 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 240 - 265 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 80 | °C |
| Source GMD, last updated:12/14/1999 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |