S-Plastics Geloy EXGY007 resin is Lowest gloss extrusion grade GELOY XTW. Will be commercialized as XTWE230
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 28 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 32 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 2.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 80 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1790 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 55 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1880 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 36 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 30 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 25 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 50 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 2 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 20 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 16 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 85 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 75 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.03E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 86 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 89 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 77 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.12 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar, flow (2) | 3 - 5 | % | S-Plastics Method |
| Mold Shrinkage, flow, 3.2 mm | 3 - 5 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 3 - 5 | % | S-Plastics Method |
| Melt Flow Rate, 200°C/3.8 kgf | 5 | g/10 min | ASTM D 1238 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 4 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:02/15/2004 | |||
| • Barrel temperatures should be banked TO 150°C (300°F) | ||
| Parameter | ||
| Sheet Extrusion | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Minimum Moisture Content | 0.02 - 0.3 | % |
| Melt Temperature | 205 - 215 | °C |
| Barrel - Zone 1 Temperature | 175 - 205 | °C |
| Barrel - Zone 2 Temperature | 175 - 205 | °C |
| Barrel - Zone 3 Temperature | 175 - 205 | °C |
| Barrel - Zone 4 Temperature | 175 - 205 | °C |
| Adapter Temperature | 150 - 205 | °C |
| Die Temperature | 150 - 205 | °C |
| Source GMD, last updated:02/15/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Geloy EXGY007.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|