S-Plastics Geloy EXGY0057 resin is Improved ASA/PC blend for high impact, 1.5mm V0 applications. Improved UV performance aesthetically and physically compared to alternatives.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 61 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 57 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 62 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D 638 |
| Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2250 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 700 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 118 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 26 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 58 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate A/50 | 111 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 103 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 104 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 99 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 88 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Melt Flow Rate, 220°C/10.0 kgf | 32 | g/10 min | ASTM D 1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 29 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 21 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 138 | Pa-s | ISO 11443 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-1 Flame Class Rating (3)(4) | 1.2 | mm | UL 94 by GE |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:03/14/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 230 - 270 | °C |
| Nozzle Temperature | 220 - 260 | °C |
| Front - Zone 3 Temperature | 230 - 270 | °C |
| Middle - Zone 2 Temperature | 220 - 260 | °C |
| Rear - Zone 1 Temperature | 200 - 230 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 50 - 70 | °C |
| Source GMD, last updated:03/14/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Geloy EXGY0057.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|