S-Plastics Xenoy XL1339U resin is Data generated in BOZ labs. High heat grade for nonchemical resistance required applications. UV-stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 49 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2090 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2090 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | ASTM D 1044 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 699 | J/m | ASTM D 256 |
| Izod Impact, notched, 0°C | 672 | J/m | ASTM D 256 |
| Izod Impact, notched, -20°C | 598 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 245 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 224 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -10°C | 38 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| CTE, -30°C to 30°C, flow | 7.56E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 7.92E-05 | 1/°C | ASTM D 696 |
| Thermal Conductivity | 0.18 | W/m-°C | ASTM C 177 |
| Vicat Softening Temp, Rate A/50 | 140 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 130 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.22 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.1 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 0.7 | % | ASTM D 570 |
| Water Absorption, 50% RH, equilib | 0.2 | % | ASTM D 570 |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.5 - 0.8 | % | S-Plastics Method |
| Poisson's Ratio | 0.4 | - | ASTM D 638 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 4 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+14 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm | 16.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.1 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 |
| Source GMD, last updated:01/05/2000 | |||
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy XL1339U.pdf |
|