S-Plastics Xenoy XLG2400 resin is Low Gloss Xenoy, providing inherent low gloss on almost every type of tool surfaces. This grade has excellent low temperature impact, high heat resistant and is UV stabilized. Many colors available. Pls refer to the low gloss processing guidelines for optimal low gloss.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 44 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.1 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 103 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1730 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 67 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1850 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 122.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1940 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 68 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1770 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 578 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 513 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 40 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 47 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 52 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 129 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 102 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.65E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 9.78E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 7.65E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.78E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 129 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 128 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 97 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.8 - 1 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 17.5 | g/10 min | ASTM D 1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.08 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 17 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:12/06/2006 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 280 | °C |
| Nozzle Temperature | 255 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 255 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.3 - 0.6 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 50 - 80 | % |
| Vent Depth | 0.013 - 0.02 | mm |
| Source GMD, last updated:12/06/2006 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Xenoy XLG2400.pdf |
|