S-Plastics Xenoy XR100 resin is ian unfilled PBT+PC blend containing post-industrial recycle, and is suitable for injection moulding applications which require ductility down to 0C.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 20 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 17 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 15 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 1.1E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 120 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.7 - 1 | % | S-Plastics Method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 17 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:1993/09/14 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 270 | °C |
| Nozzle Temperature | 250 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 240 - 265 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 80 | °C |
| Source GMD, last updated:1993/09/14 | ||
For more information please download the datasheet | |
 | S-Plastics Xenoy XR100.pdf |