S-Plastics Verton DX08333 resin is an internally lubricated compound based on Lexan* Polycarbonate resin. Added features of this material
include: ESD Safe, PTFE-free Wear & Friction solution and balanced mechanical performance
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 72 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 7300 | MPa | ASTM D 638 |
| Flexural Stress | 99 | MPa | ASTM D 790 |
| Flexural Modulus | 6100 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 113 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7310 | MPa | ISO 527 |
| Flexural Stress | 113 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6760 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 296 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 17 | J | ASTM D 3763 |
| Multiaxial Impact | 10 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 22 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 138 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.9E-05 | 1/°C | ASTM E 831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.32 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 |
| Mold Shrinkage, flow | 0.35 | % | S-Plastics Method |
| Mold Shrinkage, xflow | 0.5 | % | S-Plastics Method |
| Wear Factor Washer | 80 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.E+06 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Source GMD, last updated:2009/01/08 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/01/08 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton DX08333.pdf |
|