S-Plastics Verton RX09010 resin is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of
this material include; Thermal Conductive, Non-Brominated & Non-Chlorinated Flame Retardant, Easy Molding.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 94 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.4 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 139 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 1 | W/m-°C | ASTM E 1530 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 192 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow (5) | 0.2 - 0.4 | % | S-Plastics Method |
| Density | 1.72 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Glow Wire Flammability Index 960°C, passes at | 1.6 | mm | IEC 60695-2-12 |
| Source GMD, last updated:2009/07/02 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 255 - 265 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 60 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/07/02 | ||