S-Plastics Verton Cycolac_EXCP0153 resin is PRELIMINARY DATA. Antistatic ABS. Automotive, household, electronics.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 37 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 27 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 33.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1630 | MPa | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1630 | MPa | ASTM D 638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1790 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 368 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 37 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 88 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 72 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.05 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.45 - 0.65 | % | S-Plastics Method |
| Melt Flow Rate, 230°C/3.8 kgf | 18.5 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 4.E+11 | Ohm | ASTM D 257 |
| Source GMD, last updated:02/10/2003 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 6 | hrs |
| Maximum Moisture Content | 0.01 | % |
| Melt Temperature | 195 - 230 | °C |
| Nozzle Temperature | 195 - 230 | °C |
| Front - Zone 3 Temperature | 210 - 220 | °C |
| Middle - Zone 2 Temperature | 200 - 210 | °C |
| Rear - Zone 1 Temperature | 170 - 180 | °C |
| Mold Temperature | 50 - 70 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Shot to Cylinder Size | 50 - 70 | % |
| Vent Depth | 0.038 - 0.051 | mm |
| Source GMD, last updated:02/10/2003 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton Cycolac_EXCP0153.pdf |
|