S-Plastics Verton PX07437 resin is Compound based on Nylon 6 resin containing glass fiber and impact modifier.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 97 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 94 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5200 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 150 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4650 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1070 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 200 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 5 | J | ASTM D 3763 |
| Instrumented Impact Total Energy, 23°C | 25 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.23 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 - 0.9 | % | ASTM D 955 |
| Source GMD, last updated:07/10/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 275 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:07/10/2008 | ||