S-Plastics Verton PX08000 resin is a compound based on PA6 resin containing Impact Modifier. Added features include : High Impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 50 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 78 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 6.7 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 1900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.02E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 151 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 57 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 1.4 | % | S-Plastics Method |
| Water Absorption, 23°C/24hrs | 2.2 | % | ISO 62-1 |
| Source GMD, last updated:05/21/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 275 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:05/21/2008 | ||
Other related products we recommend:
For more information please download the datasheet | |
 | S-Plastics Verton PX08000.pdf |
Get The Latest Quotation |