S-Plastics Verton PFD06 resin is a compound based on Nylon 6 resin containing Glass Fiber, Carbon Powder. Added features of this material
include: Electrically Conductive.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 159 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11720 | MPa | ASTM D 638 |
| Flexural Stress | 241 | MPa | ASTM D 790 |
| Flexural Modulus | 11030 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 907 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 206 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.43 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.5 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.38 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.15 | % | ISO 294 |
| Moisture Absorption (23°C / 50% RH) | 0.91 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+03 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+00 - 6.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:2005/08/02 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 275 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2005/08/02 |
|
For more information please download the datasheet |
|
 |
S-Plastics Verton PFD06.pdf |
|