S-Plastics LEXAN CFR9111 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated
flame retardant PC has an UL-94 V0 rating at 1.5 mm and good flow capability. LEXAN CFR9111 is available in clear
transparent and tinted color options that is an excellent candidate for a wide variety of applications.
| MECHANICAL | TYPICAL VALUES | UNITS | TEST METHODS |
| Tensile Stress, yld, Type I, 50 mm/min | 67 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 80 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 103 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2400 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 73 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 96 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| IMPACT | |||
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D 4812 |
| Izod Impact, unnotched, -30°C | NB | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 600 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 103 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 80 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 55 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 9 | kJ/m² | ISO 180/1A |
| Drying Temperature | 120 | °C |
| Drying Time | 3 – 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 280 – 305 | °C |
| Nozzle Temperature | 275 – 300 | °C |
| Front - Zone 3 Temperature | 280 – 305 | °C |
| Middle - Zone 2 Temperature | 270 – 295 | °C |
| Rear - Zone 1 Temperature | 260 – 280 | °C |
| Mold Temperature | 70 – 95 | °C |
| Back Pressure | 0.3 – 0.7 | MPa |
| Screw Speed | 40 – 70 | rpm |
| Shot to Cylinder Size | 40 – 60 | % |
| Vent Depth | 0.025 – 0.076 | mm |
|
For more information please download the datesheet |
|
 |
S-Plastics LEXAN CFR9111.pdf |
|